In this study, two types of fatigue tests were conducted. First, cyclic bending tests were performed using the micro-bending tester. A four-point bending test method was adopted, because it induces uniform stress fields within a loading span. Second, thermal fatigue tests were conducted using a pseudo power cycling machine which was newly developed for a realistic testing condition. The pseudo-power cycling method makes up for the weak points in a power cycling and a chamber cycling method. Two compositions of solder are tested in all test condition, one is lead-free solder (95.5Sn4.0Ag0.5Cu) and the other is eutectic lead-contained solder (63Sn37Pb).
In the cyclic bending test, the solder that exhibits a good reliability can be reversed depending on the load conditions. The lead-contained solders have a longer fatigue life in the region where the applied load is high. On the contrary, the lead-free solder sustained more cyclic loads in the small load region. A similar trend was detected at the thermal cycling test.
A three-dimensional finite element analysis model was constructed. A finite element analysis using ABAQUS was performed to extract the applied stress and strain in the solder joints. A constitutive model which includes both creep and plasticity was employed. Thermal fatigue was occurred due to the creep. And plastic deformation is main damage for bending failure. From the inelastic energy dissipation per cycle versus fatigue life curve, it can be found that the bending fatigue life is longer than the thermal fatigue life.
In the cyclic bending test, the solder that exhibits a good reliability can be reversed depending on the load conditions. The lead-contained solders have a longer fatigue life in the region where the applied load is high. On the contrary, the lead-free solder sustained more cyclic loads in the small load region. A similar trend was detected at the thermal cycling test.
A three-dimensional finite element analysis model was constructed. A finite element analysis using ABAQUS was performed to extract the applied stress and strain in the solder joints. A constitutive model which includes both creep and plasticity was employed. Thermal fatigue was occurred due to the creep. And plastic deformation is main damage for bending failure. From the inelastic energy dissipation per cycle versus fatigue life curve, it can be found that the bending fatigue life is longer than the thermal fatigue life.
목차
Abstract
1. 서론
2. 실험장치 및 실험 결과
3. 유한요소해석
4. 결론
후기
참고문헌
참고문헌 (0)
참고문헌 신청함께 읽어보면 좋을 논문
논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!
-
무연솔더(SnAgCu)와 유연솔더(SnPb)의 피로 수명 비교 연구
대한기계학회 논문집 A권
2004 .12
-
박막 광학 필터 디바이스의 패키징시 솔더 조인트의 피로 신뢰성 해석
대한기계학회 논문집 A권
2004 .06
-
BGA 형태 솔더 접합부의 피로 수명 예측에 관한 연구
한국생산제조학회지
2008 .02
-
A Study on μBGA Solder Joints Reliability Using Lead-free Solder Materials
Journal of Mechanical Science and Technology
2002 .07
-
솔더 접합부의 피로 수명 예측 연구
한국생산제조학회 학술발표대회 논문집
2007 .05
-
열충격에 따른 Pb-Free Solder의 Low Cycle Fatigue 특성
대한용접학회 특별강연 및 학술발표대회 개요집
2013 .11
-
Sn/3.5Ag/0.75Cu와 63Sn/37Pb 소더 조인트의 복합하중하의 피로 거동 특성 평가
대한기계학회 춘추학술대회
2002 .03
-
열 피로 하중을 받는 유/무연 솔더의 확률론적 신뢰성 평가
대한기계학회 춘추학술대회
2006 .06
-
Void 가 무연솔더 접합부의 피로수명에 미치는 영향
대한기계학회 춘추학술대회
2005 .05
-
Energy Partitioning Approach를 이용한 Solder Joint의 열 피로 수명 예측
한국자동차공학회 춘 추계 학술대회 논문집
2006 .06
-
솔더 조인트의 열사이클 특성에 관한 연구
한국재료학회 학술발표대회
1997 .01
-
63Sn-37Pb 땜납의 크리프 특성에 관한 연구
Journal of the Korean Society for Precision Engineering
2004 .02
-
자동차용 엔지니어링 플라스틱의 내구해석용 피로물성 도출에 관한 연구
한국자동차공학회 추계학술대회 및 전시회
2009 .11
-
Effect of Thermal Conductivity on its Thermal Fatigue Behavior of Solder Joints under Power Cycling Condition
대한기계학회 춘추학술대회
2004 .08
-
솔더접합부 접합구조에 따른 열사이클 시험 예측
한국정밀공학회 학술발표대회 논문집
2011 .06
-
CAE를 이용한 자동차용 휠(wheel)의 피로수명 예측기법 연구
한국자동차공학회논문집
2004 .03
-
Sn-Ag-Cu-X 무연솔더로 솔더링 된 접합부의 진동파괴 거동
대한용접·접합학회지
2012 .04
-
무은 솔더의 신뢰성 평가에 관한 연구
신뢰성응용연구
2013 .06
-
절연 저항변화에 따른 솔더 조인트의 건전성 평가
대한기계학회 춘추학술대회
2004 .08
-
무연솔더를 이용한 μBGA 솔더접합부의 열피로수명 예측 ( Thermal Fatigue Life Prediction of μBGA Solder Joint Using Lead-free Solder Materials )
대한용접학회 특별강연 및 학술발표대회 개요집
2001 .01
이 논문의 저자 정보
이 논문과 함께 이용한 논문
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2009-550-016788338