Purpose : UHMWPE (Ultra-high-molecular-weight-polyethylene) is one of the most widely used material in knife protection clothes because of high strength, elasticity, and light weight. The purpose of this study is to develop the accelerated life test method and predict the lifetime for the knife protection fabric composed by UHMWPE.
Methods : In this study, degradation characteristics of UHMWPE fibers and knife protection fabric for cut resistance were evaluated under the hydrolysis and photo-degradation conditions. It was found out that the degradation rate of retained tensile strength was more significant in the photo-degradation than hydrolysis. Therefore, the failure time was determined as the time that the retained tensile strength in photo-degradation is less than 50%. Considering an acceleration factor for irradiance and exposure time, the lifetime was predicted from the calculated failure time.
Results : As a result of the accelerated life test, the B10 lifetime of knife protection fabric composed by UHMWPE fibers is estimated as 2.8 years for a 90% statistical confidence level.
Conclusion: Since the lifetime is predicted by the view-point of radiant exposure in this study, there is a possibility that the estimated lifetime may differ from the actual lifetime. However, it is considered as an useful methodology to estimate the long-term lifetime of knife protection fabrics.
Methods : In this study, degradation characteristics of UHMWPE fibers and knife protection fabric for cut resistance were evaluated under the hydrolysis and photo-degradation conditions. It was found out that the degradation rate of retained tensile strength was more significant in the photo-degradation than hydrolysis. Therefore, the failure time was determined as the time that the retained tensile strength in photo-degradation is less than 50%. Considering an acceleration factor for irradiance and exposure time, the lifetime was predicted from the calculated failure time.
Results : As a result of the accelerated life test, the B10 lifetime of knife protection fabric composed by UHMWPE fibers is estimated as 2.8 years for a 90% statistical confidence level.
Conclusion: Since the lifetime is predicted by the view-point of radiant exposure in this study, there is a possibility that the estimated lifetime may differ from the actual lifetime. However, it is considered as an useful methodology to estimate the long-term lifetime of knife protection fabrics.
목차
1. 서론
2. 평가시료
3. 내환경성평가(가속인자 도출)
4. 가속수명시험
5. 결론
참고문헌
참고문헌 (10)
참고문헌 신청
[학술지(정기간행물)] - 정기수 / 2008 / 방검복 특성및 성능평가 기술 / 섬유기술과산업 4 (12) : 247 ~ 252
[학술지(정기간행물)] - 한설아 / 2008 / 보호복 관련 국내·외 표준에 대한 탐색적 조사 - ISO, ASTM, CEN, KS를 중심으로 - / 한국의류산업학회지 10 (1) : 92 ~ 100
[학술지(정기간행물)] - Li, C. S. / 2012 / Degradation behavior of ultra-high molecular weight polyethylene fibers under artificial accelerated weathering / Polymer Testing 31 : 938 ~ 943
[단행본] - Martin, J. W. / 2008 / Service Life Prediction of Polymeric Materials:Global Perspectives / Springer : 71 ~ 82
[학술지(정기간행물)] - Vu Thi, B. N. / 2009 / Mechanics and Mechanism of Cut Resistance of Protective Materials / Theoretical and Applied Fracture Mechanics 52 : 7 ~ 13
[학술지(정기간행물)] - 한설아 / 2008 / 보호복 관련 국내·외 표준에 대한 탐색적 조사 - ISO, ASTM, CEN, KS를 중심으로 - / 한국의류산업학회지 10 (1) : 92 ~ 100
[학술지(정기간행물)] - Li, C. S. / 2012 / Degradation behavior of ultra-high molecular weight polyethylene fibers under artificial accelerated weathering / Polymer Testing 31 : 938 ~ 943
[단행본] - Martin, J. W. / 2008 / Service Life Prediction of Polymeric Materials:Global Perspectives / Springer : 71 ~ 82
[학술지(정기간행물)] - Vu Thi, B. N. / 2009 / Mechanics and Mechanism of Cut Resistance of Protective Materials / Theoretical and Applied Fracture Mechanics 52 : 7 ~ 13
함께 읽어보면 좋을 논문
논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!
-
로봇용감속기의 내구성능평가장치를 위한 소프트웨어 개발 및 가속내구시험 프로토콜 제안
대한기계학회 춘추학술대회
2019 .02
-
전투화용 고무의 가속수명예측
한국산학기술학회 논문지
2015 .12
-
복합 고장 유형을 가지는 변압기에 대한 수명추정
신뢰성응용연구
2022 .12
-
보행시험 데이터를 활용한 군사용 착용형 로봇 감속기 수명주기 산출
신뢰성응용연구
2023 .06
-
몬테카를로 시뮬레이션을 이용한 부품이 원형으로 배열된 k-out-of-n: G 균형 시스템의 수명분포 추정
신뢰성응용연구
2025 .03
-
Accelerated Lifetime Test Based on Mathematical Method for Light-emitting Electrochemical Cells
한국고분자학회 학술대회 연구논문 초록집
2016 .04
-
임무 종료 후 폐기 준비를 위한 태양활동에 따른 궤도 수명 예측
한국항공우주학회 학술발표회 초록집
2015 .11
-
종속적 관계를 갖는 혼합구조에 대한 경쟁적 위험모형의 구축
산업경영시스템학회지
2017 .01
-
철도차량 1차 현가장치용 고무스프링 사용수명 예측모델 개발
한국도시철도학회논문집
2019 .03
-
변화점 회귀모델을 이용한 연료접촉 고무오링의 수명예측
신뢰성응용연구
2020 .09
-
커패시터의 제조사 보증 수명과 가속열화시험을 통한 실제 수명 비교
대한기계학회 춘추학술대회
2021 .04
-
가속열화시험을 이용한 고무 복합체의 저장수명 예측
한국추진공학회 학술대회논문집
2019 .05
-
수명시험 적용을 고려한 전계해석에 대한 연구
대한전기학회 학술대회 논문집
2022 .07
-
Lifetime Assessment for Oil-Paper Insulation using Thermal and Electrical Multiple Degradation
Journal of Electrical Engineering & Technology
2017 .03
-
A Lifetime Estimation Method of MMC Submodules Based on the Combination of FEA and Physical Lifetime Model
ICPE(ISPE)논문집
2019 .05
-
Lifetime Assessment Method using Multiple-Stress Acceleration Aging for Flexible Cable of Portable Electric Machines
Journal of Electrical Engineering & Technology
2016 .09
-
이기종 프로세서 사용수명을 고려한 신경망 가속 스케쥴링
대한전자공학회 학술대회
2022 .11
-
성능특성치의 열화가 대수정규분포를 따를 때의 가속열화시험 모형 개발
신뢰성응용연구
2018 .03
-
가속파괴열화시험을 통한 연료접촉 고무오링의 수명예측
신뢰성응용연구
2019 .09
-
이기종프로세서 사용수명 신뢰성 평가를 위한 모델링 방법론
대한전자공학회 학술대회
2022 .11
이 논문의 저자 정보
이 논문과 함께 이용한 논문
가전 제품용 세라믹 히터의 수명 및 고장 원인에 대한 연구
최형석
신뢰성응용연구
2017
.12
구조화 마코프체인을 이용한 이종 구성품을 갖는 k-out-of-n 시스템의 수명분포 모형
김흥섭
신뢰성응용연구
2017
.12
철도차량 접촉기의 신뢰성 분석 및 교환주기 결정에 대한 연구
박민흥
,
이세헌
신뢰성응용연구
2017
.12
무기체계의 고장 이력 데이터를 활용한 소프트웨어 신뢰도 분석 모델 적용 사례 연구
조일훈
,
황성국
,
이익도
외 3명
신뢰성응용연구
2017
.12
베이지안 기법에 기반한 수명자료 분석에 관한 문헌 연구 : 2000~2016
원동연
,
임준형
,
심현수
외 3명
신뢰성응용연구
2017
.09
최근 본 자료
댓글(0)
0