The thermo-mechanical interaction between brake block and wheel tread during braking has been found to cause thermal crack on the wheel tread. Due to thermal expansion of the rim material, the thermal cracks will protrude from the wheel tread and be more exposed to wear during the wheel/block contact than the rest of the tread surface.
The wheel rim is in residual compression stress when is new. After service running, the region in the tread has reversed to tension. This condition can lead to the formation and growth of thermal cracks in the rim which can ultimately lead to premature failure of wheel. In the present paper, the thermal cracks of railway wheel, one of severe damages on the wheel tread, were evaluated to understand the safety of railway wheel in running condition.
The residual stresses for damaged wheel which are applied to tread brake are investigated. Mainly X-ray diffusion method is used. Under the condition of concurrent loading of continuous rolling contact with rails and cyclic frictional heat from brake blocks, the reduction of residual stress is found to correlate well with the thermal crack initiation.
The wheel rim is in residual compression stress when is new. After service running, the region in the tread has reversed to tension. This condition can lead to the formation and growth of thermal cracks in the rim which can ultimately lead to premature failure of wheel. In the present paper, the thermal cracks of railway wheel, one of severe damages on the wheel tread, were evaluated to understand the safety of railway wheel in running condition.
The residual stresses for damaged wheel which are applied to tread brake are investigated. Mainly X-ray diffusion method is used. Under the condition of concurrent loading of continuous rolling contact with rails and cyclic frictional heat from brake blocks, the reduction of residual stress is found to correlate well with the thermal crack initiation.
목차
ABSTRACT
1. 서론
2. 차륜의 잔류응력과 열손상
3. 시험방법 및 절차
4. 시험결과 및 고찰
5. 결론
참고문헌
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
이 논문과 함께 이용한 논문
지하철용 고속전동차의 진동원 및 개선대책
박기수
,
최연선
한국철도학회 학술발표대회논문집
2007
.11
대차프레임의 중량감소를 위한 형상최적설계에 관한 연구
조우석
,
최경호
,
박정호
외 2명
한국정밀공학회 학술발표대회 논문집
2000
.10
도시철도차량의 안전진단평가 기법에 관한 연구
정종덕
,
한석윤
,
박기준
외 1명
한국정밀공학회 학술발표대회 논문집
2005
.06
UIC code에 따른 대차 프레임 구조해석 및 시험에 관한 연구
최중호
,
송시엽
,
천홍정
외 2명
한국철도학회 학술발표대회논문집
2002
.10
고속열차 동력차의 센터피봇 상대 회전각 계측에 관한 연구
서승일
,
정우진
한국철도학회 논문집
2006
.06
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2013-326-001083725