It has been very important in various industry fields to improve the fatigue strength characteristics of bearings such as bearing life, fatigue limit, etc., because such poor properties could result in shortening the machinery life as well as in decreasing the accuracy. However, no successful heat treatment criterion seems to be available at present.
In this study, the effect of the 170℃×120min tempering cycles repeated after 830℃×30min oil quenching for 800℃ spheroidizing-annealed bearing steel (STB2) as base metal on the 120℃ high temperature rotary bending fatigue strength characteristics were investigated, including the effects on hardness, Charpy impact value and micro-structure, in order to seek for the best heat treatment condition finally. The important results obtained are as follows :
1) The optimal cycle of tempering so that the fatigue strength σ could become the highest was the 4th cycle. And it is confirmed that this σ<SUB>F</SUB> is about 6 times more increased than that of base metal, and about 1.3 times more increased than the case of the 1 cycle tempered.
2) As a result of the investigation for the effects of tempering cycles on hardness, the hardness at the tempering number of 2 thru 5 cycles was not decreased severely ; only about 10% decrease from those of the quenched and 1 cycle tempered case. Such hardness is equivalent to H<SUB>R</SUB>C61~62 with no bad effect on anti-abrasion of bearing steel.
3) In the case of 2 thru 5 cycle tempering as well as 1 cycle tempering, the impact value was not so improved comparing with the case of quenching, but an increase of 5 to 10% could be expected at least.
4) It was experimentally confirmed that the control of the mechanical properties improvement such as fatigue strength and fatigue life for bearing steels could be possible by the number of tempering cycles.
In this study, the effect of the 170℃×120min tempering cycles repeated after 830℃×30min oil quenching for 800℃ spheroidizing-annealed bearing steel (STB2) as base metal on the 120℃ high temperature rotary bending fatigue strength characteristics were investigated, including the effects on hardness, Charpy impact value and micro-structure, in order to seek for the best heat treatment condition finally. The important results obtained are as follows :
1) The optimal cycle of tempering so that the fatigue strength σ could become the highest was the 4th cycle. And it is confirmed that this σ<SUB>F</SUB> is about 6 times more increased than that of base metal, and about 1.3 times more increased than the case of the 1 cycle tempered.
2) As a result of the investigation for the effects of tempering cycles on hardness, the hardness at the tempering number of 2 thru 5 cycles was not decreased severely ; only about 10% decrease from those of the quenched and 1 cycle tempered case. Such hardness is equivalent to H<SUB>R</SUB>C61~62 with no bad effect on anti-abrasion of bearing steel.
3) In the case of 2 thru 5 cycle tempering as well as 1 cycle tempering, the impact value was not so improved comparing with the case of quenching, but an increase of 5 to 10% could be expected at least.
4) It was experimentally confirmed that the control of the mechanical properties improvement such as fatigue strength and fatigue life for bearing steels could be possible by the number of tempering cycles.
목차
Abstract
1. 서론
2. 시험편 및 실험방법
3. 결과 및 고찰
4. 결론
참고문헌
참고문헌 (0)
참고문헌 신청함께 읽어보면 좋을 논문
논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!
-
뜨임처리 온도에 따른 고장력강의 피로 및 기계적 물성평가
대한기계학회 춘추학술대회
2010 .11
-
[論文] STS 420 스테인레스 강의 기계적 성질 및 피로균열전파에 미치는 템퍼링 온도의 영향
오토저널
1992 .08
-
[論文] 鋼材의 衝擊疲勞破壞壽命에 미치는 Tempering 效果에 관한 硏究
오토저널
1981 .12
-
조질강의 표면완성처리가 피로강도에 미치는 영향 ( Effect of Surface Finishing Treatments on The Fatigue Strength of Tempered Steel )
대한기계학회지
1967 .01
-
템퍼링에 따른 Cu 첨가 고강도강의 미세조직과 기계적 특성
한국재료학회지
2014 .01
-
고경도 철계 장갑재의 미세조직과 기계적 특성 분석
한국재료학회지
2018 .01
-
Mobile camera window의 기계적 강도 향상에 관한 연구
한국기계가공학회 춘추계학술대회 논문집
2015 .10
-
구조용 중탄소강 SM45C의 열처리에 따른 기계적 성질변화
산업기술연구 : 강원대학교 산업기술연구소
1986 .01
-
C 함량이 다른 A487 주강품의 열처리 조건에 따른 기계적 및 부식 특성
한국주조공학회지 (주조)
2015 .01
-
고강도 소재의 인장과 저주기피로 물성치의 연관성에 관한 연구
소성·가공
2014 .04
-
Cr-Mo계 금형강의 기계적 성질에 미치는 합금원소 및 템퍼링의 영향
열처리공학회지
2012 .01
-
박판 스프링용 탄소공구강대(SK5M)의 기계적 성질에 미치는 뜨임 온도의 영향
한국정밀공학회 학술발표대회 논문집
2006 .05
-
강화피막을 가진 금속 의 저주기부터 초고주기까지의 피로강도 해석
대한기계학회 춘추학술대회
2020 .07
-
Fatigue Characteristics of Bearing Steel in Giga Cycles
대한기계학회 춘추학술대회
2007 .10
-
경도로부터 재료의 피로물성 추정을 통한 구름베어링 피로수명해석
한국트라이볼로지학회 학술대회
2014 .10
-
SNCM220 강 권축의 침탄 열처리를 통한 피로 강도 개선에 관한 연구
한국자동차공학회 춘 추계 학술대회 논문집
1996 .11
-
고장력강 판재의 초음파 피로시험 시편 설계
한국생산제조학회 학술발표대회 논문집
2015 .04
-
Effects of Tempering and PWHT on Microstructures and Mechanical Properties of SA508 GR.4N Steel
Nuclear Engineering and Technology
2014 .01
-
Direct Quenched Ultra-High Strength Steel: 미세조직, 인장 및 고주기 피로 특성에 미치는 reduction rate 제어 영향
한국소성가공학회 학술대회 논문집
2020 .06
-
저주기 피로에 미치는 온도의 영향
대한기계학회 춘추학술대회
2009 .04
이 논문의 저자 정보
이 논문과 함께 이용한 논문
냉각매질에 따른 열처리 변형에 관한 연구
이옥규
,
안민주
,
김경환
외 2명
한국기계가공학회 춘추계학술대회 논문집
2012
.06
초음파 나노 표면 개질(UNSM) 기술에 따른 베어링강의 VHCF 특성
서창민
,
안영동
,
서민수
외 1명
한국해양환경·에너지학회 학술대회논문집
2012
.05
SCM415강의 열처리 변형제어를 위한 냉각 매질의 특성
안민주
,
류성기
한국기계가공학회지
2010
.12
SM53C강의 고주파열처리 후 인장특성 및 평면변형률 파괴인성평가에 관한 연구
임만배
,
전현배
,
송태훈
외 1명
한국동력기계공학회 학술대회 논문집
2007
.06
침탄질화처리재의 피로수명평가
송삼홍
,
이상훈
한국정밀공학회 학술발표대회 논문집
1995
.05
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2009-559-015515305