In this study, K(Ta,Nb)O3 coating solutions were synthesized by sol-gel method using Potassium acetate, Tantalum ethoxide, Niobium ethoxide and 2-Methoxyethanol as the solvent. And K(Ta0.40Nb0.60)O3/K(Ta0.60Nb0.40)O3 heterolayered thin films were fabricated by spin-coating method on the Pt/Ti/SiO2/Si substrate. The structural and electrical properties for the application of microscale cooling devices were investigated.
K(Ta0.40Nb0.60)O3/K(Ta0.60Nb0.40)O3(KTN) heterolayered thin films were fabricated with variation of the number of coatings (3, 4, 5, 6 times). KTN heterolayered thin films showed a typical polycrystalline X-ray patterns with some pyrochlore phase. And, the effect of the lower layer on the crystallization of the upper layer can be known via the difference in the x-ray peaks depending on the coating times that is, the kind of the lower layer. Dielectric constant increases with increasing the number of KTN thin film coatings. In the P-E hysteresis loop, there is a part in which the remanent polarization value rapidly decreases as this part is shifted to a low temperature, while the number of KTN coatings increases. Electrocaloric property (△T) of the 3 times coated KTN heterolayered thin film was about 3.03℃ at room temperature.
K(Ta0.40Nb0.60)O3/K(Ta0.60Nb0.40)O3(KTN) heterolayered thin films were fabricated with variation of the number of coatings (3, 4, 5, 6 times). KTN heterolayered thin films showed a typical polycrystalline X-ray patterns with some pyrochlore phase. And, the effect of the lower layer on the crystallization of the upper layer can be known via the difference in the x-ray peaks depending on the coating times that is, the kind of the lower layer. Dielectric constant increases with increasing the number of KTN thin film coatings. In the P-E hysteresis loop, there is a part in which the remanent polarization value rapidly decreases as this part is shifted to a low temperature, while the number of KTN coatings increases. Electrocaloric property (△T) of the 3 times coated KTN heterolayered thin film was about 3.03℃ at room temperature.
목차
제 1 장 서론 1제 2 장 이론 62.1 K(Ta,Nb)O3 강유전 세라믹 62.2 유전 특성 92.3 복합 재료의 유전 상수 112.4 전기열량효과 12제 3 장 실험 143.1 CSD법을 이용한 K(Ta,Nb)O3 이종층 박막의 제작 143.1.1 K(Ta,Nb)O3 전구체 제작 143.1.2 K(Ta,Nb)O3 이종층 박막 제작 153.2 K(Ta,Nb)O3 이종층 박막의 특성 측정 183.2.1 구조적 특성 183.2.2 전기적 특성 19제 4 장 결과 및 고찰 214.1 구조적 특성 214.1.1 K(Ta,Nb)O3 이종층 박막의 X-ray 회절 분석 214.1.1 K(Ta,Nb)O3 이종층 박막의 표면 특성 234.1.1 K(Ta,Nb)O3 이종층 박막의 단면 특성 234.2 전기적 특성 274.2.1 K(Ta,Nb)O3 이종층 박막의 유전상수 및 유전손실 274.2.2 K(Ta,Nb)O3 이종층 박막의 분극-전계 이력 곡선 344.2.3 K(Ta,Nb)O3 이종층 박막의 분극-온도 곡선 364.2.4 K(Ta,Nb)O3 이종층 박막의 전기열량 온도 변화 (T) 39제 5 장 결론 42참고 문헌 43