초록· 키워드
오류제보하기
Crack is the cause of impairing the safety of the structure. Since long ago, many researchers have studied to solve the crack problem. In other words, crack propagation rates such as brittle fracture, fatigue fracture, and stress corrosion cracking were analyzed. In addition, there have been many studies on the threshold stress intensity factor (), which is the limit stress of crack initiation, but the micro-crack problem that can be applied uniformly to various failure modes has not been solved.
This study was evaluated threshold stress intensity factor and fatigue limit of short cracks. Two equations used. That is, the crack length dependence equation of suggested by Tange et al with modification of Haddad et al''s equation, and the crack length dependence equation of suggested by Ando et al considering the plastic zone dimensions. The two equations showed similar tendencies despite the different basic viewpoints. In addition, the equation of Ando et al was able to quantitatively evaluate the threshold stress intensity factor and fatigue limit despite of the difference in the specimen size, crack aspect ratio, and stress ratio.
Therefore, this study proved that the structures safety for various materials and failure modes can be evaluated by Ando et al''s equation.
This study was evaluated threshold stress intensity factor and fatigue limit of short cracks. Two equations used. That is, the crack length dependence equation of suggested by Tange et al with modification of Haddad et al''s equation, and the crack length dependence equation of suggested by Ando et al considering the plastic zone dimensions. The two equations showed similar tendencies despite the different basic viewpoints. In addition, the equation of Ando et al was able to quantitatively evaluate the threshold stress intensity factor and fatigue limit despite of the difference in the specimen size, crack aspect ratio, and stress ratio.
Therefore, this study proved that the structures safety for various materials and failure modes can be evaluated by Ando et al''s equation.
목차
제1장 서론 11.1 본 연구의 배경 및 목적 21.2 피로균열의 발생과 전파 특성 21.3 본 논문의 구성 및 개요 6참고문헌 8제2장 응력비가 다른 짧은 균열의 하한계응력확대계수와 피로한도 평가 132.1 서언 142.2 재료 및 평가방법 162.3 결과 및 고찰 222.4 결언 48참고문헌 49제3장 다른 강종에서 시험편 치수 및 형상비에 따른 하한계응력확대계수 평가 553.1 서언 563.2 재료 및 평가방법 573.3 결과 및 고찰 603.4 결언 79참고문헌 80제4장 하한계응력확대계수 식에 의한 스프링강 SUP9A의 피로한도 및 무해화 균열 길이 평가 824.1 서언 834.2 재료 및 실험 방법 844.3 평가방법 864.4 결과 및 고찰 914.5 결언 101참고문헌 102제5장 결론 105발표 논문 107감사의 글 110