초록· 키워드
오류제보하기
Purpose: The purpose of this study was to evaluate the push-out bond strength of glassfiber post cemented with different adhesive system and surface treatments.
Method: 160 tooth samples made from 48 human maxillary single-rooted teeth with similar root length were divided into 4 groups according to the adhesive system (no adhesive,
Adper Single Bond 2, Clearfil SE Bond. Clearfil S3). Each group had 4 subgroups according to the post surface treatment methods(no treatment, sandblast, silane, sandblast and silane). Posts (Parapost Fiber White) were cemented with Rely X Unicem. The teeth were
sectioned perpendicular to their long axis into 1-mm thick sections. The push-out tests was performed at a speed of 0.5mm/min. The results were evaluated by 2-way ANOVA,
1-way ANOVA and multiple comparison procedures (Tukey test) (α=0.05).
Results: Tukey test showed that the adhesive system significantly influenced the push-out strength. The Clearfil SE Bond group showed the highest value. Post surface treatments showed no significant effect.
Conclusion: Bond strength of glass-fiber post cemented with self-adhesive resin cement using Clearfil SE Bond showed significantly higher values compared to other adhesive systems.
Method: 160 tooth samples made from 48 human maxillary single-rooted teeth with similar root length were divided into 4 groups according to the adhesive system (no adhesive,
Adper Single Bond 2, Clearfil SE Bond. Clearfil S3). Each group had 4 subgroups according to the post surface treatment methods(no treatment, sandblast, silane, sandblast and silane). Posts (Parapost Fiber White) were cemented with Rely X Unicem. The teeth were
sectioned perpendicular to their long axis into 1-mm thick sections. The push-out tests was performed at a speed of 0.5mm/min. The results were evaluated by 2-way ANOVA,
1-way ANOVA and multiple comparison procedures (Tukey test) (α=0.05).
Results: Tukey test showed that the adhesive system significantly influenced the push-out strength. The Clearfil SE Bond group showed the highest value. Post surface treatments showed no significant effect.
Conclusion: Bond strength of glass-fiber post cemented with self-adhesive resin cement using Clearfil SE Bond showed significantly higher values compared to other adhesive systems.
목차
Ⅰ.서론 1Ⅱ.재료 및 방법 51. 연구 재료 52. 연구 방법 63. 통계분석 8Ⅲ.결과 10Ⅳ.고찰 13Ⅴ.결론 16참고문헌 17ABSCTRACT 20