The purpose of this study was to investigate to effect of the ZrN coated on surface property and corrosion resistance and physical property of dental casting alloys using various instruments.
The specimens were used, respectively, for experiment, Arc Ion plating was carried out for dentel casting alloys using ZrN coated materials with nitrogen gas. ZrN coated surface property of each specimen was observed with field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), atomic force microscopy (AFM), micro vickers hardness tester, nano indentation tester and electrochemical tester. The surface of ZrN coated specimen was more smooth than that of other kinds of non-coated specimen. ZrN coated surface showed higher hardness than that of non-coated surface.
The corrosion potential of the ZrN coated specimen was comparatively high. The current density of ZrN coated specimen was smaller than that of non-coated specimen in 0.9% NaCl solution at 36.5 ± 1℃
The specimens were used, respectively, for experiment, Arc Ion plating was carried out for dentel casting alloys using ZrN coated materials with nitrogen gas. ZrN coated surface property of each specimen was observed with field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), atomic force microscopy (AFM), micro vickers hardness tester, nano indentation tester and electrochemical tester. The surface of ZrN coated specimen was more smooth than that of other kinds of non-coated specimen. ZrN coated surface showed higher hardness than that of non-coated surface.
The corrosion potential of the ZrN coated specimen was comparatively high. The current density of ZrN coated specimen was smaller than that of non-coated specimen in 0.9% NaCl solution at 36.5 ± 1℃
목차
1. 서 론 12. 이론적 배경2.1 박막의 미세구조 42.2 Ion plating법의 특징 82.3 Ion plating 의 장점 92.4 Ion plating 의 종류 102.5 ZrN의 특징 133. 실험방법3.1 코팅시편 제작 153.2 주조 합금의 주조 방법에 따른 표면분석 193.3 시편의 ZrN Arc Ion plating 103.4 코팅 층 특성 분석 213.4.1 코팅된 Co-Cr 합금의 표면 형상 및 미세조직 분석 213.4.2 표면 경도 시험 213.4.3 표면 거칠기 조사 213.5 전기화학적 부식 시험 224. 연구결과 및 고찰4.1 주조 합금의 주조 방법에 따른 표면형상 244.2 코팅 층 특성 274.2.1 ZrN 코팅된 치과용Co-Cr 합금의 표면형상 274.2.2 ZrN 코팅된 치과용 Co-Cr 합금의 미세구조 294.2.3 Zrn 코팅된 치과용 Co-Cr 합금의 표면경도 324.2.4 ZrN 코팅된 치과용 Co-Cr 합금의 표면거칠기 354.3 ZrN 코팅된 치과용 Co-Cr 합금의 부식거동조사 385. 고 찰 506. 결 론 51REFERENCES 52Abstract 53