Recently, one of the hydrogen production methods has attracted using dense metallic membrane. It has high hydrogen permeation and selectivity which hardly could adopt industrial product because of high cost, hydrogen embrittlment and thermal stability. Meanwhile, vanadium has high hydrogen solubility and it use to instead of Pd-Ag amorphous membrane. Aluminum carried out blocking hydrogen diffusion on grain boundary therefore protecting hydrogen embrittlement. Most of dense metallic membrane is solution diffusion mechanism. The solution diffusion mechanism was very similar hydrogen storing steps such as steps of metal hydride. Thus, V-Al composites were fabricated to use hydrogen induced mechanical alloying. The fabricated V-Al composites were characterized by XRD, SEM, EDS and simultaneous TG/DSC analyses. The hydrogenation behaviors were evaluated using a Sievert`s type automatic PCT apparatus. The hydrogenation behaviors of V-Al composites was evaluated too low hydrogen stored capacity and fast hydrogenation kinetics. In PCI results, V-Al composites had low hydrogen solubility, in spite of that, hydrogen kinetics was calculated very fast and hydrogen absorption/desorption contents were same capacity.
목차
등록된 정보가 없습니다.
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
최근 본 자료
댓글(0)
0