This study was to add crushed frit with different grain sizes to 3Y-TZP so that it could determine the mechanical properties depending on sintering temperature. In this study, 3 types specimens were prepared in powder with respective additions of 20wt.% frit, which was sized through 24-, 48- and 72-hour ball milling with zirconia. Then, sintered pellets were tested in experiments under the temperature variations for different compositions. As a result, this study came to the following findings: 1. It was found that the higher sintering temperature and the longer ball milling time of frit led to the higher sintered density. 2. Bending strength tended to increase with higher sintering temperature and longer ball milling time of frit. 3. Hardness tended to increase with higher sintering temperature and longer ball milling time of frit. 4. However, it was found that fracture toughness didn't vary significantly depending on sintering temperature. From these findings, it was concluded that the smaller frit grain size and the narrower particle size distribution of frit lead to the better mechanical properties.
목차
등록된 정보가 없습니다.
참고문헌 (0)
참고문헌 신청함께 읽어보면 좋을 논문
논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!
-
Zirconia-Frit composites의 소결 및 물성에 미치는 MgO 첨가의 효과
대한치과기공학회지
2010 .01
-
3Y-지르코니아 조성에서 glass frit의 첨가량에 따른 소결 거동 및 기계적 특성의 변화
치위생과학회지
2009 .01
-
Development of High Strength All-glass Porcelains Prepared with Two Types of Zirconium-containing Frit
대한치과재료학회 학술대회
2004 .08
-
마이크로웨이브 소결방법에 따른 치과용 지르코니아의 물리적 특성
대한치과기공학회지
2012 .01
-
치과용 지르코니아 도재의 LiO 첨가에 따른 열팽창계수 변화
대한치과기공학회지
2009 .01
-
Effects of the sintering conditions of dental zirconia ceramics on the grain size and translucency
The Journal of Advanced of Prosthodontics
2013 .01
-
Fracture Toughness of 3Y-TZP Ceramics Sintered by Microwave Furnace
대한치과재료학회 학술대회
2011 .05
-
Microwave sintering한 치과용 3Y-TZP 소결체의 기계적 특성
대한치과재료학회 학술대회
2007 .06
-
Technical Factors Affecting the Properties of Dental Zirconia
대한치과재료학회 학술대회
2011 .05
-
CAD/CAM지르코니아 재료의 특성
대한치과의사협회지
2011 .05
-
Comparison of the optical properties of pre-colored dental monolithic zirconia ceramics sintered in a conventional furnace versus a microwave oven
The Journal of Advanced of Prosthodontics
2017 .01
-
Sintering behavior and mechanical properties of zirconia compacts fabricated by uniaxial press forming
The Journal of Advanced of Prosthodontics
2010 .01
-
치과용 Co-Cr sinter metal의 소결 후 변형비교
대한치과기공학회지
2016 .01
-
다층 지르코니아 블록 종류와 소결방법에 따른 지르코니아 코핑의 파절강도와 색조 비교
대한치과기공학회지
2019 .01
-
반복소성이 도재의 결합강도에 미치는 영향
대한치과재료학회지
2015 .12
-
치관보철용 Hydroxyapatite의 기계적 물성에 미치는 pH 및 반응온도의 영향
대한치과기공학회지
2004 .01
-
치과용 지르코니아 블록의 소결온도에 따른 기계적 특성과 색조변화
대한치과기공학회지
2017 .01
-
치과 CAD/CAM용 지르코니아의 소결 시 계류시간이 굴곡강도에 미치는 영향
대한치과재료학회지
2016 .06
-
Effect of hydrofluoric acid-based etchant at an elevated temperature on the bond strength and surface topography of Y-TZP ceramics
Restorative Dentistry and Endodontics
2020 .01
이 논문의 저자 정보
최근 본 자료
댓글(0)
0