In this study, nano-sized cobalt oxide powder with an average particle size below 50 nm was prepared from a cobalt chloride solution by the spray pyrolysis process. The influences of reaction temperature on the properties of the generated powder were examined. The average particle size of the particles formed based on the spray pyrolysis process at a reaction temperature of $700^{\circ}C$ is roughly 20 nm. Moreover, most of these particles cannot appear with an independent type, thereby coexisting in a droplet type. When the reaction temperature increases to $800^{\circ}C$, the average particle size not only increases to roughly 40 nm but also shows a more dense structure while the ratio of particles which shows a polygonal form significantly increases. As the reaction temperature increases to $900^{\circ}C$, the distribution of the particles is from roughly 70 nm to 100 nm, while most of the particle surface is more intricately close and forms a polygonal shape. When the reaction temperature increases to $1000^{\circ}C$, the particle size distribution of the powder shows an existing form from 80 nm to at least 150 nm in an uneven form. As the reaction temperature increases, the XRD peak intensity gradually increases, yet the specific surface area gradually decreases.
목차
등록된 정보가 없습니다.
참고문헌 (13)
참고문헌 신청
T. Nakamura / 1996 / Proceeding of the ICF 7 :C1~101
C. P. Udawatte / 2001 / J. Am. Ceram. Soc. 84(1):251
유재근 / 2013 / Infleunce of Nozzle Tip Size on the Preparation of Nano-Sized Tin Oxide Powder by Spray Pyrolysis Process / 한국재료학회지 23(2):81~88
J. K. Yu / 2013 / Powder Tech. 235(2):1030
J. K. Yu / 2012 / J. of Nanosci. Nanotechnol. 12(2):1545
C. P. Udawatte / 2001 / J. Am. Ceram. Soc. 84(1):251
유재근 / 2013 / Infleunce of Nozzle Tip Size on the Preparation of Nano-Sized Tin Oxide Powder by Spray Pyrolysis Process / 한국재료학회지 23(2):81~88
J. K. Yu / 2013 / Powder Tech. 235(2):1030
J. K. Yu / 2012 / J. of Nanosci. Nanotechnol. 12(2):1545
이 논문의 저자 정보
최근 본 자료
댓글(0)
0