To investigate the adhesion effect of sodium bisulfite content in making blocked isocyanate, wood adhesive PB-1, PB-2, PB-3 and PB-4 containing sodium bisulfite content of 15%, 22.5%, 30% and 37.5% were synthesized respectively. As a result, when the amount of sodium bisulfite increased in adhesives, the tensile strength was found to be proportionally increased. The final adhesive mixtures were manufactured using a two-components system which are prepared by mixing two separate protein and BI solutions due to the precipitate in the adhesives. As PVA was added to adhesives to increase tenacity, the plywood dehiscence phenomenon after cold pressing process was declined. By addition of PVA, the tensile strength was improved up to $6.5{\sim}7kgf/cm^2$ with BI/protein ratio from 1:6 up to 1:8. Phase separation between milk fat and aqueous layer was disappeared after addition of emulsifier, Tween 20. Additon of Tween 20 showed tensile strength up to $5{\sim}6.5 kgf/cm^2$ at NCO/protein ratio of 1:12 ~ 1:14 without phase separation.
목차
등록된 정보가 없습니다.
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
최근 본 자료
댓글(0)
0