To improve sensing capability of infrared, heat-resistance and mechanical properties, the $SiO_2$ and $TiO_2$ anti-reflective layers were coated on sapphire substrate by MOCVD. The standard wavelength was 4,600nm, and the thickness of anti-reflective layers were 379 and 758nm in case of ${\lambda}/4$ and ${\lambda}/2$ of incident angle($65^{\circ}$), respectively. The $SiO_2$ and $TiO_2$ anti-reflective layers were coated 12.6 and 9.7nm/min of deposition rates by increasing oxygen pressure to set the ideal refractive index of 1.283. In case of $SiO_2({\lambda}/2)$ coating, the transmittance increased from 55.0 to 62.7%. The transmittance of $TiO_2({\lambda}/2)$ anti-reflective layer also increased from 55.0 to 64.8%. The flexural strength of $SiO_2({\lambda}/2)$ and $TiO_2({\lambda}/2)$ layer coated sapphire increased from 337.8 to 362.9 and 371.8MPa, respectively. The flexural strength at $500^{\circ}C$ of these materials also increased respectively to 304.5, 358.2MPa from 265.9MPa. From these results, we confirmed these materials can be used as transmission window of infrared light.
목차
등록된 정보가 없습니다.
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
최근 본 자료
댓글(0)
0