A comparative study was performed on the microstructures and the mechanical properties of STD11 and 8Cr steel. The specimens were quenched from $1030^{\circ}C$ and tempered at $240^{\circ}C$ and $520^{\circ}C$. Vickers hardness, impact toughness and tensile tests were conducted at various tempering temperatures. Microstructural characterization to measure grain size, volume fraction of retained austenite and distribution of carbides was carried out by using SEM, EBSD, TEM and X-ray diffraction techniques. Due to finer $M_7C_3$ carbides dispersed, 8Cr steel showed larger impact toughness and plasticity than STD11 irrespective of the tempering temperature. While 8Cr steel had lower hardness in as-quenched state and after tempering at $240^{\circ}C$ owing to smaller carbide content and more retained austenite, it was harder after tempering at $520^{\circ}C$ due to larger precipitation hardening from finer $M_{23}C_6$.
목차
등록된 정보가 없습니다.
참고문헌 (23)
참고문헌 신청
이 논문의 저자 정보
최근 본 자료
댓글(0)
0