Isothermal transformation behavior of a 10% Cr heat resistant steel fabricated by centrifugal casting process was investigated. Normalized specimen at $1100^{\circ}C$ for 1 hour was isothermally annealed at temperature range between $600^{\circ}C$ and $700^{\circ}C$ with various time. The annealed specimen had eutectoid structure which was generated along austenitic grain boundary during isothermal annealing. Areal fraction of eutectoid structure increased up to 25% after holding at $700^{\circ}C$ for 20 hours. It was observed that austenitic matrix was transformed to ferrite structure and fine $M_{23}C_6$ carbides with increase of annealing time. Time-temperature-transformation diagram of the centrifugally cast 10% Cr steel with 0.18 wt% C was plotted based on the results of isothermal transformation behavior.
목차
등록된 정보가 없습니다.
참고문헌 (11)
참고문헌 신청
강창룡 / 2011 / 페라이트상을 갖는 12Cr 내열강의 기계적성질에 미치는 템퍼링 처리의 영향 / 한국동력기계공학회지 15(2):49~54
J. M. Vitek / 1983 / Metallurgical Transactions A 14A:1047
강창룡 / 2009 / 원심주조된 내열강의 미세조직 및 기계적성질에 미치는 단조 조건의 영향 / 한국동력기계공학회지 13(3):47~52
S. M. Lee / 2010 / J. of the Korean Society for Power System Engineering 14(2):84
김주업 / 2011 / 대한금속재료학회 2011년도 추계학술발표대회 :157
J. M. Vitek / 1983 / Metallurgical Transactions A 14A:1047
강창룡 / 2009 / 원심주조된 내열강의 미세조직 및 기계적성질에 미치는 단조 조건의 영향 / 한국동력기계공학회지 13(3):47~52
S. M. Lee / 2010 / J. of the Korean Society for Power System Engineering 14(2):84
김주업 / 2011 / 대한금속재료학회 2011년도 추계학술발표대회 :157
이 논문의 저자 정보
최근 본 자료
댓글(0)
0