This study has been investigated for tensile properties with lead-free brass containing 1 wt.% of Bi. And also characteristic of corrosion resistance was analyzed by polarization test. An increase of tempering temperature was found to tend to decrease tensile strength, and percentage of elongation was shown to be the lowest value at $300^{\circ}C$. On the other hand, the elongation was increased with an increase of tempering temperature after $300^{\circ}C$. The change of mechanical properties was closely related with the content and shape of acicular Witmanst$\ddot{a}$tten ${\alpha}$ formed at the interface of ${\beta}$ phase as well as in ${\beta}$ phase. Tensile strength had a tendency to be decreased with an increase of test temperature. The elongation was shown to be the lowest value at around $300^{\circ}C$, while it began to increase as test temperature rose after $300^{\circ}C$. It might be speculated that the reason that elongation was decreased was found to form bismuth film at the interface of ${\alpha}/{\beta}$ phase leading to be easily brittle when loaded by tensile stress. The lead-free brass containing 1 wt.% of Bi had similar characteristic of corrosion resistance with a free-cutting brass with 3.4 wt. % of Pb in spite of higher fraction of ${\beta}$ phase.
목차
등록된 정보가 없습니다.
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
최근 본 자료
댓글(0)
0