The crystallization effects of boron (B) powder on the phase, full width at half maximum (FWHM) values, and critical properties were investigated for in-situ reacted $MgB_2$ bulk superconductors. The semi-crystalline B powder was heat-treated at different temperatures of 1000, 1300 and $1500^{\circ}C$ for 5 hours in an Ar atmosphere. Then, using as-received and heat-treated B powders, the $MgB_2$ samples were prepared at $600^{\circ}C$ for 40 hours in an Ar atmosphere. As the heat-treatment temperature of the B powder increased, both the particle size of the B powder and crystalline phase increased. In the case of $MgB_2$ samples using B powders heat-treated at above $1300^{\circ}C$, unreacted magnesium (Mg) and B remained due to the improved crystallinity of the B powder. As the heat-treatment temperature of B powder increased, the critical current density of $MgB_2$ decreased continuously due to the reduction of grain boundary density and superconducting volume caused by unreacted Mg and B.
목차
등록된 정보가 없습니다.
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
최근 본 자료
댓글(0)
0