수계 Cu 나노입자 잉크에서 Poly(styrene-co-maleic acid) 접착 증진제가 잉크 레올로지와 인쇄패턴의 접착력에 미치는 영향

조예진; 서영희; 정선호; 최영민; 김의덕; 오석헌; 류병환

추천

검색

자료유형: 학술저널

저자정보: 조예진 (한국화학연구원 그린화학소재본부) 서영희 (한국화학연구원 그린화학소재본부) 정선호 (한국화학연구원 그린화학소재본부) 최영민 (한국화학연구원 그린화학소재본부) 김의덕 (한화중앙연구소, 나노R&D센터) 오석헌 (한화중앙연구소, 나노R&D센터) 류병환 (한국화학연구원 그린화학소재본부)

저널정보: 한국재료학회 한국재료학회지 한국재료학회지 제25권 제12호

발행연도: 2015.1

수록면: 719 - 726 (8page)

이용수

📌

연구주제

📖

연구배경

🔬

연구방법

🏆

연구결과

초록· 키워드

오류제보하기

For a decade, solution-processed functional materials and various printing technologies have attracted increasingly the significant interest in realizing low-cost flexible electronics. In this study, Cu nanoparticles are synthesized via the chemical reduction of Cu ions under inert atmosphere. To prevent interparticle agglomeration and surface oxidation, oleic acid is incorporated as a surface capping molecule and hydrazine is used as a reducing agent. To endow water-compatibility, the surface of synthesized Cu nanoparticles is modified by a mixture of carboxyl-terminated anionic polyelectrolyte and polyoxylethylene oleylamine ether. For reducing the surface tension and the evaporation rate of aqueous Cu nanoparticle inks, the solvent composition of Cu nanoparticle ink is designed as DI water:2-methoxy ethanol:glycerol:ethylene glycol = 50:20:5:25 wt%. The effects of poly(styrene-co-maleic acid) as an adhesion promoter(AP) on rheology of aqueous Cu nanoparticle inks and adhesion of Cu pattern printed on polyimid films are investigated. The 40 wt% aqueous Cu nanoparticle inks with 0.5 wt% of Poly(styrene-co-maleic acid) show the "Newtonian flow" and has a low viscosity under $10mPa{\cdots}S$, which is applicable to inkjet printing. The Cu patterns with a linewidth of $50{\sim}60{\mu}m$ are successfully fabricated. With the addition of Poly(styrene-co-maleic acid), the adhesion of printed Cu patterns on polyimid films is superior to those of patterns prepared from Poly(styrene-co-maleic acid)-free inks. The resistivities of Cu films are measured to be $10{\sim}15{\mu}{\Omega}{\cdot}cm$ at annealing temperature of $300^{\circ}C$.

#aqueous Cu nanoparticle ink #inkjet printing #poly #styrene-co-maleic acid) #rheology #adhesion of printed Cu pattern

참고문헌 (0)

참고문헌 신청

참고문헌이 DBpia에서 서비스 중이라면, [참고문헌 신청]을 통해 등록해보세요

함께 읽어보면 좋을 논문

논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!

이 논문의 저자 정보

조예진

소속기관 한국화학연구원 그린화학소재본부

주요연구분야 공학 > 재료·에너지공학 > 재료공학 공학 > 화학공학 > 고분자공학

논문수 10 이용수 76

서영희

소속기관 한국화학연구원 그린화학소재본부