Pt nanoparticle catalysts incorporated on $RuO_2$ nanowire support were successfully synthesized and their electrochemical properties, such as methanol electro-oxidation and electrochemically active surface (EAS) area, were demonstrated for direct methanol fuel cells (DMFCs). After fabricating $RuO_2$ nanowire support via an electrospinning method, two different types of incorporated Pt nanoparticle electrocatalysts were prepared using a precipitation method via the reaction with $NaBH_4$ as a reducing agent. One electrocatalyst was 20 wt% Pt/$RuO_2$, and the other was 40 wt% Pt/$RuO_2$. The structural and electrochemical properties of the Pt nanoparticle electrocatalysts incorporated on electrospun $RuO_2$ nanowire support were investigated using a bright field transmission electron microscopy (bright field TEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and cyclic voltammetry. The bright field TEM, XRD, and XPS results indicate that Pt nanoparticle electrocatalysts with sizes of approximately 2-4 nm were well incorporated on the electrospun $RuO_2$ nanowire support with a diameter of approximately 50 nm. The cyclic voltammetry results showed that the Pt nanoparticle catalysts incorporated on the electrospun $RuO_2$ nanowire support give superior catalytic activity in the methanol electro-oxidation and a higher electrochemically active surface (EAS) area when compared with the electrospun Pt nanowire electrocatalysts without the $RuO_2$ nanowire support. Therefore, the Pt nanoparticle catalysts incorporated on the electrospun $RuO_2$ nanowire support could be a promising electrode for direct methanol fuel cells (DMFCs).
목차
등록된 정보가 없습니다.
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
최근 본 자료
댓글(0)
0