[ $WO_3$ ]powders were ball-milled with an alumina ball for 0-72 hours. $In_2O_3$ doped $WO_3$ was prepared by soaking ball-milled $WO_3$ in an $InCl_3$ solution. The mixed powder was annealed at $700^{\circ}C$ for 30 min in an air atmosphere. A paste for screen-printing the thick film was prepared by mixing the $WO_3$:In2O3 powders with ${\alpha}$-terpinol and glycerol. $In_2O_3$ doped $WO_3$ thick films were fabricated into a gas sensor by a screen-printing method on alumina substrates. The structural properties of the $WO_3$:$InO_3$ thick films were a monoclinic phase with a (002) dominant orientation. The particle size of the $WO_3$:$InO_3$ decreased with the ball-milling time. The sensing characteristics of the $In_2O_3$ doped $WO_3$ were investigated by measuring the electrical resistance of each sensor in the test-box. The highest sensitivity to 5 ppm $CH_4$ gas and 5 ppm $CH_3CH_2CH_3$ gas was observed in the ball-milled $WO_3$:$InO_3$ gas sensors at 48 hours. The response time of $WO_3$:$In_2O_3$ gas sensors was 7 seconds and recovery time was 9 seconds for the methane gas.
목차
등록된 정보가 없습니다.
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
최근 본 자료
댓글(0)
0