In the segmented-in-series solid-oxide fuel cells (SIS-SOFCs), fabrication techniques which use decalcomania paper have many advantages, i.e., an increased active area of the electrode; better interfacial adhesion property between the anode, electrolyte and cathode; and improved layer thickness uniformity. In this work, a cell-stack was fabricated on porous ceramic flattened tube supports using decalcomania paper, which consists of an anode, electrolyte, and a cathode. The anode layer was $40{\mu}m$ thick, and was porous. The electrolyte layers exhibited a uniform thickness of about $20{\mu}m$ with a dense structure. Interfacial adhesion was improved due to the dense structure. The cathode layers was $30{\mu}m$ thick with porous structure, good adhesion to the electrolyte. The ohmic resistance levels at 800, 750 and $700^{\circ}C$ were measured, showing values of 1.49, 1.58 and $1.65{\Omega}{\cdot}cm^2$, respectively. The polarization resistances at 800, 750 and $700^{\circ}C$ were measured to be 1.63, 2.61 and $4.17cm^2$, respectively. These lower resistance values originated from the excellent interfacial adhesion between the anode, electrolyte and cathode. In a two-cell-stack SOFC, open-circuit voltages(OCVs) of 1.915, 1.942 and 1.957 V and maximum power densities(MPD) of 289.9, 276.1 and $220.4mW/cm^2$ were measured at 800, 750 and $700^{\circ}C$, respectively. The proposed fabrication technique using decalcomania paper was shown to be feasible for the easy fabrication of segmented-in-series flattened tube SOFCs.
목차
등록된 정보가 없습니다.
참고문헌 (13)
참고문헌 신청
안용태 / 2012 / 전사지를 이용 적층한 셀 구조 및 연료극 기능층 형성에 따른 출력 특성 / 한국재료학회지 22(11):626~630
박성태 / 2011 / 고체산화물연료전지 연결재용 La_0.7Ca_0.3Cr_0.9Co_0.1O_(3-δ) 조성계에 Ca Source 변화에 따른 소결 및 전기적 특성에 관한 연구 / 한국세라믹학회지 48(3):246~250
S. C. Singhal / 2002 / Solid State Ionics 152:405
G. A. Tompsett / 2000 / J. Power Sources 86:376
T. Fukui / 2004 / J. Power Sources 125:17
박성태 / 2011 / 고체산화물연료전지 연결재용 La_0.7Ca_0.3Cr_0.9Co_0.1O_(3-δ) 조성계에 Ca Source 변화에 따른 소결 및 전기적 특성에 관한 연구 / 한국세라믹학회지 48(3):246~250
S. C. Singhal / 2002 / Solid State Ionics 152:405
G. A. Tompsett / 2000 / J. Power Sources 86:376
T. Fukui / 2004 / J. Power Sources 125:17
이 논문의 저자 정보
최근 본 자료
댓글(0)
0