The particle size of MgO was examined as a function of the Na content in $Mg(OH)_2$ powders and the calcination temperature. $Mg(OH)_2$ suspension was obtained by dropwise precipitation of $Mg(NO_3)_2{\cdot}6H_2O$ and NaOH solutions. The suspension was diluted by varying the dilution volume ratio of distilled water to $Mg(OH)_2$ suspension to change the Na salt concentration in the suspension. $Mg(OH)_2$ slurry was filtered and dried at $60^{\circ}C$ under vacuum, and then its $Mg(OH)_2$ powder was calcined to produce MgO with different amount of Na content at $500\sim900^{\circ}C$ under air. Investigation of the physical and chemical properties of the various MgO powders with dilution ratio and calcination temperature variation was done by X-ray diffraction, transmission electron microscopy, BET specific surface area and thermal gravimetric analysis. It was observed that MgO particle size could depend on the condition of calcination temperature and dilution ratio of the $Mg(OH)_2$ suspension. The particle size of the MgO depends on the Na content remaining in the $Mg(OH)_2$ powder, which powder was prepared by changing the dilution ratio of the $Mg(OH)_2$ suspension. This change increased as the calcination temperature increased and decreased as the dilution ratio increased. The growth of MgO particle size according to the increase of temperature was more effective when there was a relatively high content of Na. The increase of Na content lowered the temperature at which decomposition of $Mg(OH)_2$ to MgO took place, thereby promoting the crystal growth of MgO.
목차
등록된 정보가 없습니다.
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
최근 본 자료
댓글(0)
0