수용성 매체에서 뮬라이트의 합성거동 및 입자형상에 미치는 염 및 전구체 pH의 영향

정연길; 이재언; 신영일; 김재원; 조창용

추천

검색

자료유형: 학술저널

저자정보: 정연길 (창원대학교 재료공학과) 이재언 (창원대학교 재료공학과) 신영일 (창원대학교 재료공학과) 김재원 (창원대학교 재료공학과) 조창용 (한국기계연구원 내열재료그룹)

저널정보: 한국재료학회 한국재료학회지 한국재료학회지 제13권 제4호

발행연도: 2003.1

수록면: 251 - 258 (8page)

이용수

📌

연구주제

📖

연구배경

🔬

연구방법

🏆

연구결과

초록· 키워드

오류제보하기

The effects of the salt and the precursor pH on the synthesizing behavior and the morphology of mullite have been studied. Two kinds of mullite precursor sols were prepared by the dissolution of two kinds of salt (aluminum nitrate enneahydrate, Al($NO_3$)$_3$ㆍ$9H_2$O; type I and aluminum sulfate 14∼18 water, (SO$Al_4$)$_3$$\cdot$$14∼18H_2$O; type II) into the mixture of colloidal silica sol, respectively. Precursor pH of the sols was controlled to the acidic (pH= 1.5∼2) and basic (pH= 8.5∼9) conditions. The co-products with nitrate and sulfate were completely eliminated at $500^{\circ}C$ and $850^{\circ}C$, respectively, which was confirmed by TG/DTA results. The synthesizing temperature of mullite phase was found to be above $1200^{\circ}C$ for pH= 1.5∼2 and above $1300^{\circ}C$ for pH= 8.5∼9 in type I. However, in type II, the synthesizing temperature of mullite was decreased to $850^{\circ}C$ for pH= 1.5∼2 and $1100^{\circ}C$ for pH= 8.5∼9. The grain size of the mullite synthesized at pH= 8.5∼9 was larger than that at pH= 1.5∼2 in overall heat-treated temperatures, showing smaller grain size in type II. Aspect ratio of the mullite grains was more increased at pH= 1.5∼2 than pH= 8.5∼9 in type I, showing similar aspect ratio at both pH conditions in type II. It was found that the synthesizing temperature and grain size were predominantly governed by the initial precursor pH and decomposition of the salt, with minor effect on the grain morphology.

#Mullite #precursor ph #salt #synthesizing temperature #grain morphology #grain size

참고문헌 (0)

참고문헌 신청

참고문헌이 DBpia에서 서비스 중이라면, [참고문헌 신청]을 통해 등록해보세요

함께 읽어보면 좋을 논문

논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!