$Gd_2$$O_3$:Eu phosphor particles with nano-sized and non-aggregation characteristics were prepared by spray pyrolysis using the spray solution containing polymeric precursor and $Li_2$$CO_3$ flux material. Nano-sized $Gd_2$$O_3$:Eu phosphor particles had higher brightness than the commercial $Y_2$$O_3$:Eu phosphor particles. The $Gd_2$$O_3$:Eu phosphor particles had nano-size and non-aggregation characteristics after heat-treatment at $1000^{\circ}C$ when the addition amount of $Li_2$$CO_3$ flux was 1 wt.% and 3 wt.%. The mean size of particles were 200 nm and 400 nm when the amount of flux was 1 wt.% and 3 wt.%, respectively. The prepared phosphor particles had higher photoluminescence intensity than that of the commercial product regardless of the content of$ Li_2$$CO_3$ flux and had the maximum brightness when the content of flux was 5 wt %. The photoluminescence intensity of the nano-sized $Gd_2$$O_3$:Eu phosphor particles containing 3 wt.% $Li_2$$CO_3$ flux was 125% in comparison with that of the micron-sized $Y_2$$O_3$:Eu commercial product.
목차
등록된 정보가 없습니다.
참고문헌 (0)
참고문헌 신청함께 읽어보면 좋을 논문
논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!
-
분무열분해 공정에 의해 합성된 미세 GdO:Eu 형광체의 발광 특성
화학공학
2008 .01
-
융제 및 고분자 첨가 용액으로부터 분무 열분해 공정에 의해 합성한 YO:Eu 형광체
화학공학
2005 .01
-
분무열분해법에 의해 제조되어진 $(Sr,Ca)_{10}(PO_4)_6:Eu^{2+}$형광체 분말의 형태 및 발광특성
한국재료학회 학술발표대회
2001 .01
-
분무열분해 공정에서 붕소 농도에 따른 GdO:Eu 형광체의 GdBO:Eu 형광체로의 전환
한국재료학회지
2006 .01
-
EFFECT OF THE VAR10US CODOPANTS ON THE LUMINESCENT PROPERTIES OF $Y_2$$O_3$:Eu PHOSPHORS
한국재료학회 학술발표대회
1998 .01
-
Preparation and Surface treatment of Spherical $BaMgAl_{10}O_{17}:Eu^{2+}$ phosphor
한국정보디스플레이학회 International Meeting
2004 .01
-
분무열분해법에서 유기 첨가물에 의한 $Y_2O_3:Eu$형광체 분말의 형태 및 발광 특성 향상
한국재료학회 학술발표대회
2001 .01
-
분무열분해 공정에 의해 합성된 유로피움이 도핑된 YBO 형광체의 진공자외선 하에서의 발광 특성
한국재료학회지
2006 .01
-
Synthesis and Luminescent Characteristics of $BaGa_{2}S_{4}:Eu^{2+}$ Phosphor by Solid-state Method
Journal of information display
2006 .01
-
분무열분해법에서 BAM($Ba_xMg_yAl_zO_m$) 형광체의 발광 특성
한국재료학회 학술발표대회
2002 .01
-
분무열분해 공정에 의해 제조된 BaSrSiO:Eu 형광체의 발광특성
화학공학
2006 .01
-
The Effect of Addition of Gd, La into $YVO_{4}:Eu^{3+}$ Red Phosphor
한국정보디스플레이학회 International Meeting
2003 .01
-
Synthesis and characterization of $Y_2O_3$:Eu nano phosphor powder by a new technique
한국정보디스플레이학회 International Meeting
2006 .01
-
(Ba,Sr)$_2SiO_4:Eu^{2+}$ Phosphor Particles by Spray Pyrolysis Process
한국정보디스플레이학회 International Meeting
2002 .01
-
Nano-sized $Gd_{2}O_{3}:Eu$ phosphor particles of high brightness
한국정보디스플레이학회 International Meeting
2003 .01
-
Effect of $Bi^{3+}$ addition on photoluminescence of (Y,Gd)(V,P)$O_4$:Eu phosphor
한국정보디스플레이학회 International Meeting
2008 .01
-
분무열분해법에서 Eu의 농도변화에 따른 BAM 형광체의 발광 특성
한국재료학회 학술발표대회
2001 .01
-
적색 형광체 나노 분말의 합성 및 특성 평가
공업화학
2008 .01
-
초음파 분무법으로 제조한 $(Y,Gd)BO_3:Eu^{3+}$ 형광체의 발광특성에 관한 연구
한국재료학회지
2000 .01
-
분무열분해 공정의 제조 조건이 CaMg(SiO)Cl:Eu 형광체 특성에 미치는 영향
한국재료학회지
2008 .01
이 논문의 저자 정보
최근 본 자료
댓글(0)
0