A new manufacturing process of Fe-Cr-Al powder porous metal was attempted. First, ultra-fine fecralloy powders were produced by using the submerged electric wire explosion process. Evenly distributed colloid (0.05~0.5%powders) was dispersed on PU (Polyurethane) foam through the electrospray process. And then degreasing and sintering processes were conduced. In order to examine the effect of sintering temperature in process, pre-samples were sintered for two hours at temperatures of 1350oC, 1400oC, 1450oC, and 1500oC, respectively, in H2 atmospheres. A 24-hour TGA (thermo gravimetric analysis) test was conducted at 1000oC in a 79% N2+21% O2 to investigate the high temperature oxidation behavior of powder porous metal. The results of the high temperature oxidation tests showed that oxidation resistance increased with increasing sintering temperature (2.57% oxidation weight gain at 1500oC sintered specimen).
The high temperature oxidation mechanism of newly manufactured Fe-Cr-Al powder porous metal was also discussed.
목차
등록된 정보가 없습니다.
참고문헌 (18)
참고문헌 신청
이 논문의 저자 정보
최근 본 자료
댓글(0)
0