This study investigated refinement behaviors of TiC powders produced under different impact energy conditions using a mechanical milling process. The initial coarse TiC powders with an average diameter of 9.3 μm were milled for 5, 20, 60 and 120 mins through the conventional low energy mechanical milling (LEMM, 22G) and specially designed high energy mechanical milling (HEMM, 65G). TiC powders with angular shape became spherical one and their sizes decreased as the milling time increased, irrespective of milling energy. Based upon the FE-SEM and BET results of milled powders, it was found initial coarse TiC powders readily became much finer near 100 nm within 60 min under HEMM,while their sizes were over 200 nm under LEMM, despite the long milling time of up to 120 min. Particularly, ultra-fine TiC powders with an average diameter of 77 nm were fabricated within 60 min in the presence of toluene under HEMM.
목차
등록된 정보가 없습니다.
참고문헌 (21)
참고문헌 신청
이 논문의 저자 정보
최근 본 자료
댓글(0)
0