Metal foams have a cellular structure consisting of a solid metal containing a large volume fraction ofpores. In particular, open, penetrating pores are necessary for industrial applications such as in high temperature filtersand as a support for catalysts. In this study, Fe foam with above 90% porosity and 2 millimeter pore size was successfullyfabricated by a slurry coating process and the pore properties were characterized. The Fe and Fe2O3 powdermixing ratios were controlled to produce Fe foams with different pore size and porosity. First, the slurry was preparedby uniform mixing with powders, distilled water and polyvinyl alcohol(PVA). After slurry coating on the polyurethane(PU) foam, the sample was dried at 80oC. The PVA and PU foams were then removed by heating at 700oC for 3hours. The debinded samples were subsequently sintered at 1250oC with a holding time of 3 hours under hydrogenatmosphere. The three dimensional geometries of the obtained Fe foams with an open cell structure were investigatedusing X-ray micro CT(computed tomography) as well as the pore morphology, size and phase. The coated amount ofslurry on the PU foam were increased with Fe2O3 mixing powder ratio but the shrinkage and porosity of Fe foams weredecreased with Fe2O3 mixing powder ratio.
목차
등록된 정보가 없습니다.
참고문헌 (16)
참고문헌 신청
이 논문의 저자 정보
최근 본 자료
댓글(0)
0