Steel clapping plate is used to connecting rubber body in rubber dam. However, once the steel clapping plate corrodes, it may cause faults, such as the same problems experienced by typical reinforcing steel. This study evaluated the applicability of glass fiber reinforced polymer composite(GFRP) clapping plate as a substitute for steel clapping plate. Absorption and load test were conducted to evaluate the decrease in durability of GFRP clapping plate exposed to deterioration environments.
In the durability test results, the absorption rate of GFRP clapping plate was appeared as 0.6∼1.0% in 50 day of immersion time.
Also, the fracture load decreased with accelerated degradation environment exposure. Moreover, the absorption rate in GFRP clapping plate increased as degradation progressed, reducing the fracture load.
목차
등록된 정보가 없습니다.
참고문헌 (14)
참고문헌 신청
ACI 440H / 2000 / Guide for the design and construction of concrete reinforced with FRP bars / American concrete institute committee 440
Chin, J. W / 1997 / Effects of Environmental Exposure on Fiber-Reinforced Plastic (FRP) Materials Used in Construction / Journal of Composites and Technology Research 19 (4)
Dakshinamoorthy, C / 1995 / Three-dimensional vibrations of inflatable dams / Thin-Walled Structures 21 (4) : 291 ~ 306
Dutta, P. K / 1996 / Low-Temperature and Freeze-Thaw Durability of Thick Composites / Composites Part B: Engineering 27 (3) : 371 ~ 379
Jones, F.R / 1983 / Stress Corrosion Cracking and its Implications for the Long-Term Durability of E-Glass Fiber Composites / Composites 14 (3) : 262 ~ 269
Chin, J. W / 1997 / Effects of Environmental Exposure on Fiber-Reinforced Plastic (FRP) Materials Used in Construction / Journal of Composites and Technology Research 19 (4)
Dakshinamoorthy, C / 1995 / Three-dimensional vibrations of inflatable dams / Thin-Walled Structures 21 (4) : 291 ~ 306
Dutta, P. K / 1996 / Low-Temperature and Freeze-Thaw Durability of Thick Composites / Composites Part B: Engineering 27 (3) : 371 ~ 379
Jones, F.R / 1983 / Stress Corrosion Cracking and its Implications for the Long-Term Durability of E-Glass Fiber Composites / Composites 14 (3) : 262 ~ 269
이 논문의 저자 정보
최근 본 자료
댓글(0)
0