TiO₂ nanotube was fabricated by electrochemical anodization with 95% ethylene glycol (EG) + 5% deionezed (DI) water + 0.5 wt% sodium fluoride. Then, measured the concentration of reactive oxygen species and evaluated the degradation efficiency of 4-chlorobenzoic acid (4CBA) using by high performance liquid chromatography(HPLC). Fabricated TiO₂ nanotube were characterized by X-ray diffraction (XRD) and field emission scanning electron microscopy(FE-SEM). TiO₂ nanotube was formed under the condition over 60 voltage. The diameter of TiO₂ nanotube is 135 nm and length is 18㎛ with 5 hours anodized at 80V. The concentration of reactive oxygen species increased the diameter of TiO₂ nanotube. Concentration of 4CBA was degraded by photocatalyst reaction of fabricated TiO₂ nanotube
목차
SYNOPSIS
1. 서론
2. 연구방법
3. 결과 및 고찰
4. 결론
References
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
이 논문과 함께 이용한 논문
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2015-530-002798021