In this study, in order to improve corrosion resistance and wear resistance of aluminum, surface treatment was made by anodizing with oxalic acid solution and sealing with nano-diamond powder. Average size of nano-diamond powder was 30nm. Anodizing with oxalic acid made many pores in the aluminum oxide layer. Pore size and oxide thickness were investigated by scanning electron microscope (SEM). Pore size increased as temperature increased and voltage increased. It was possible to make oxide layer with pore diameter more than 50 nm. Oxide thickness increased as temperature and voltage and treatment time increased. Oxide layer with above 10 μm thickness was made. Aluminum oxide layer with many pores was sealed by water with nano-diamond powder. Surface morphology was investigated by SEM. After sealing treatment with nanodiamond powder, corrosion resistance, wear resistance and hardness increased.
목차
Abstract
1. 서론
2. 실험방법
3. 실험결과
4. 고찰
5. 결론
References
참고문헌 (13)
참고문헌 신청
이 논문의 저자 정보
이 논문과 함께 이용한 논문
나노다이아몬드가 첨가된 윤활제의 마모 특성 연구
김승택
,
김승목
,
박태희
외 2명
Tribology and Lubricants
2014
.10
아노다이징 알루미늄 합금에 대한 다양한 코팅의 마찰 및 마멸 메커니즘
이규선
,
배성훈
,
이영제
한국트라이볼로지학회 학술대회
2009
.06
자동차용 알루미늄합금 5052-H32 마찰교반용접부의 미세조직과 기계적 특성
이광진
,
권의표
,
김재황
한국자동차공학회 춘계학술대회
2016
.05
고주파스핀들을 이용한 박판 알루미늄합금소재(Al5052-H32)의 마찰교반접합에 의한 용접성 평가
주영환
,
박영찬
,
이용문
외 2명
한국기계가공학회지
2017
.02
수소 플라즈마 처리에 따른 W, Si, Nb기반 질화물계와 W, Si기반 탄화물계 박막 위에서 나노다이아몬드 분말의 seed density 변화
장사라
,
송요승
,
백영준
외 2명
한국표면공학회 학술발표회 초록집
2016
.05
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2015-580-001658875