As the period of anti-corrosin warranty including perforation corrosion of original body sheet metal due to defects in material or factory workmanship has recently increased by automobile companies, it is a commitment from automotive component to maintain a high degree of quality and reliability. This study aims to evaluate the fatigue life of steel sheets which is used widely in the manufacture of automotive component. Fatigue life test are performed by using the specimens in the saturated water with salt. Four kinds of specimens are SGACC steel plates, SPHC steel plates, SGACC steel plates with EDC and SPHC steel plates with EDC. The following results that will be helpful to understand the static strength, fatigue life of steel plates in the saturated water with salt were obtained.(1)Regardless of EDC, all the specimens of SGACC steel plates didn"t fracture within 200 million fatigue life cycles however all the specimens of SPHC steel plate fractured within 200 million fatigue life cycles.(2)The fatigue life of the specimen of SPHC steel plates was approximately 43 percent lower than that of the specimen of SPHC steel plates with EDC. From these results, the applicability of material to the automobile component is discussed.
목차
Abstract
1. 서론
2. 부식 메카니즘 및 부식 피로 균열
3. 시험조건 및 시험방법
4. 결론
References
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
이 논문과 함께 이용한 논문
SiO₂ 나노 콜로이드 량이 다른 Si₃N₄의 열처리에 따른 마모 특성
안석환
,
남기우
대한기계학회 논문집 A권
2014
.10
후열처리형 1.5Gpa급 롤 포밍 부품 개발
김태경
,
김근호
대한용접학회 특별강연 및 학술발표대회 개요집
2014
.05
열간압연 이후 주행하는 고온 강재의 냉각해석에서 소재의 물성변화 효과 연구
박일석
,
박정은
대한기계학회 논문집 B권
2013
.05
알루미늄용접 판재의 잔류응력 측정과 해석
김진우
,
이동우
,
송정일
대한기계학회 춘추학술대회
2012
.11
알루미늄 5454 합금 판재의 성형성 예측
김찬일
,
양승한
,
김영석
대한기계학회 논문집 A권
2012
.02
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2015-550-001320598