The accelerated thermal aging of CSPE (chlorosulfonated polyethylene) was carried out for 40.41, 121.22, and 202.04 days at 100°C, which are equivalent to 20, 60, and 100years of aging at 50°C, respectively. The volume electrical resistivities of the accelerated thermally aged CSPE samples for 0, 40.41, 121.22, and 202.04 days were 1.107×1014?2.097×10<SUP>14</SUP>, 7.752×10<SUP>13</SUP>?1.556×10<SUP>14</SUP>, 7.693× 10<SUP>13</SUP>?1.521×10<SUP>14</SUP>, and 7.380×10<SUP>13</SUP>?1.304×10<SUP>14</SUP>Ω·cm, respectively, at room temperature. The permittivities of the accelerated thermally aged CSPE samples for 0, 40.41, 121.22, and 202.04 days were 2.89×10<SUP>-11</SUP>? 3.65×10<SUP>-11</SUP>, 3.40×10<SUP>-11</SUP>? 3.70×10<SUP>-11</SUP>, 3.50×10<SUP>-11</SUP>? 3.82×10<SUP>-11</SUP>, and 3.76×10<SUP>-11</SUP>? 4.13×10<SUP>-11</SUP> F/m, respectively, at room temperature. The EAB (elongation at break) of the accelerated thermally aged CSPE samples for 0, 40.41, 121.22, and 202.04 days were 98.8?101.3, 59.5?60.3, 37.8?39.2, and 41.8?44.3%, respectively, at room temperature. The apparent densities of the accelerated thermally aged CSPE samples for 0, 40.41, 121.22, and 202.04 days were 1.603?1.614, 1.611?1.613, 1.622?1.628, and 1.618?1.620g/㎤, respectively, at room temperature. The measured currents of the accelerated thermally aged CSPE and the standard sample were almost constant after 5 min of applying a 300-V/mm electric field to the CSPE. The V-I slope of the accelerated thermally aged CSPE sample was increased if the applied electric field was increased at room temperature, and the V-I slope of the accelerated thermally aged CSPE was higher than that of standard CSPE.
목차
Abstract
1. Introduction
2. Experimental Procedure
3. Experimental Results and Discussion
4. Conclusions
References
참고문헌 (11)
참고문헌 신청
1. [보고서] - Korea Advanced Institute of Science and Technology, Department of Nuclear and Quantum Engineering / 2011 / Accident of Fukushima NPPs in Japan: Outcomes and impact, and lessons learned (Interim Report)
2. [학술대회논문] - Y. D. Shin / 2012 / Effects on Measuring Temperature of Volume Electrical Resistivity of the Accelerated Thermal Aging CSPE / KIEE summer conference : 1020 ~ 1021
3. [보고서] - US NRC / 2010 / Essential Elements of an Electric Cable Condition Monitoring Program
4. [학술지(정기간행물)] - K. T. Gillen / 2006 / Condition Monitoring Methods Applied to Degradation of Chlorosulfonated Polyethylene Cable Jacketing Materials / Polymer Degradation and Stability
5. [학술지(정기간행물)] - Z. Gu / 2010 / Preparation and Properties of Chlorosulfonated Polyethylene/Organomontmorillonite Nanocomposites / Journal of Applied Polymer Science
2. [학술대회논문] - Y. D. Shin / 2012 / Effects on Measuring Temperature of Volume Electrical Resistivity of the Accelerated Thermal Aging CSPE / KIEE summer conference : 1020 ~ 1021
3. [보고서] - US NRC / 2010 / Essential Elements of an Electric Cable Condition Monitoring Program
4. [학술지(정기간행물)] - K. T. Gillen / 2006 / Condition Monitoring Methods Applied to Degradation of Chlorosulfonated Polyethylene Cable Jacketing Materials / Polymer Degradation and Stability
5. [학술지(정기간행물)] - Z. Gu / 2010 / Preparation and Properties of Chlorosulfonated Polyethylene/Organomontmorillonite Nanocomposites / Journal of Applied Polymer Science
이 논문의 저자 정보
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2015-500-001097394