The objective of this paper was to evaluate the abrasive wear behavior of restorative composite resin after thermal cycling. The test materials used in this study are Synergy(SG), Filtek™ Z350 XT(Z3), GRADIA<SUP>®</SUP> DIRECT anterior(GD), Filtek™ Z250(Z2), CLEARFILL AF-X(CL), Heliomolar<SUP>®</SUP>(HM), Metafil CX(MF). Among these composite resin materials, one group was immersed in distilled water for 10 days at 37℃ while the other was subjected to thermal cycling at 5℃ and 55℃ in a water bath for 10,000 cycles. Subsequently, they were subjected to toothbrush abrasion test using a wear testing machine for 100,000 brushings under an applied normal load of 1.5 N. The surface roughness of the composite resin materials before and after abrasion testing was measured using a surface profilometer and their morphological features were assessed using scanning electron microscope (SEM). The tensile strength of the composite resin materials immersed in deionized water and those subjected to thermal cycling were evaluated using a universal testing machine.
The mean surface roughness (Ra) of the composite resin materials immersed in deionized water for 10 days at 37℃ is lesser than 0.1 ㎛ whereas SG, HM, MF subjected to thermal cycling showed Ra values higher than 0.1 ㎛ and their Ra values in comparison with other materials in the same group had a significant difference (p＜0.05). The abrasive wear behavior is obvious in the matrix of all the composite resins tested and the shape of fillers is clearly evident for those subjected to thermal cycling. The loss of filler material and the formation of cracks on the matrix as well as at the interface between the filler and the matrix are also observed for the composite resin samples subjected to thermal cycling. The tensile strength of CL is 74.6 ㎫, which is the highest value while that of Z3 and MF are 36.2 ㎫ and 37.5 ㎫, respectively, which is the lowest among all the composite resin materials immersed in deionized water. Among the composite resin materials subjected to thermal cycling, CL exhibits a higher tensile strength of 65.5 ㎫ whereas the MF offers a very low tensile strength of 16.1 ㎫, which is more than half of the value obtained for the same sample immersed in deionized water.
The mean surface roughness (Ra) of the composite resin materials immersed in deionized water for 10 days at 37℃ is lesser than 0.1 ㎛ whereas SG, HM, MF subjected to thermal cycling showed Ra values higher than 0.1 ㎛ and their Ra values in comparison with other materials in the same group had a significant difference (p＜0.05). The abrasive wear behavior is obvious in the matrix of all the composite resins tested and the shape of fillers is clearly evident for those subjected to thermal cycling. The loss of filler material and the formation of cracks on the matrix as well as at the interface between the filler and the matrix are also observed for the composite resin samples subjected to thermal cycling. The tensile strength of CL is 74.6 ㎫, which is the highest value while that of Z3 and MF are 36.2 ㎫ and 37.5 ㎫, respectively, which is the lowest among all the composite resin materials immersed in deionized water. Among the composite resin materials subjected to thermal cycling, CL exhibits a higher tensile strength of 65.5 ㎫ whereas the MF offers a very low tensile strength of 16.1 ㎫, which is more than half of the value obtained for the same sample immersed in deionized water.
목차
ABSTRACT
서론
연구재료 및 방법
결과
고찰
결론
참고문헌
참고문헌 (25)
참고문헌 신청
1. [학술지(정기간행물)] - Abouelatta OB / 2005 / Wear and surface roughness of current veneered materials after toothbrush/dentifrice abrasion / J Mater Proc Tech 168 : 431 ~ 437
2. [단행본] - Anusavice KJ / 2001 / Phillips' Science of Dental Materials / The eleventh edition of Book Inc : 399 ~ 441
3. [학술지(정기간행물)] - Baek SH / 1998 / Effect of thermal cycling and aging on the tensile strength of light-cured restorative composites / J Korean Res Soc Dent Mater 25 : 29 ~ 35
4. [학술지(정기간행물)] - Bollen CM / 1997 / Comparison of surface roughness of oral hard materials to the threshold surface roughness for bacterial plaque retention: a review of the literature / Dent Mater 13 : 258 ~ 269
5. [학술지(정기간행물)] - Braem M / 1989 / Mechanical properties and filler fraction of dental composites / Dent Mater J 5 : 346 ~ 348
2. [단행본] - Anusavice KJ / 2001 / Phillips' Science of Dental Materials / The eleventh edition of Book Inc : 399 ~ 441
3. [학술지(정기간행물)] - Baek SH / 1998 / Effect of thermal cycling and aging on the tensile strength of light-cured restorative composites / J Korean Res Soc Dent Mater 25 : 29 ~ 35
4. [학술지(정기간행물)] - Bollen CM / 1997 / Comparison of surface roughness of oral hard materials to the threshold surface roughness for bacterial plaque retention: a review of the literature / Dent Mater 13 : 258 ~ 269
5. [학술지(정기간행물)] - Braem M / 1989 / Mechanical properties and filler fraction of dental composites / Dent Mater J 5 : 346 ~ 348
이 논문의 저자 정보
이 논문과 함께 이용한 논문
열 순환과 기계적 순환이 세라믹 코더-도재 비니어의 파절 저항성에 미치는 영향
김정미
,
배지명
,
오승한
대한치과재료학회 학술대회
2013
.11
열 순환과 기계적 순환이 세라믹 코어-도재 비니어의 파절 저항성에 미치는 영향
김정미
,
배지명
,
오승한
대한치과재료학회지
2013
.12
용사법에 의한 질코니아 세라믹코팅에 대한 연구 ( Plasma Spray Coating of Zirconia Ceramic )
이형근
,
김대훈
,
황선효
외 2명
대한용접·접합학회지
1989
.06
압자의 압입에 의한 치관 전장용 복합레진의 기계적 성질 평가
최원호
,
배태성
,
박광선
외 1명
대한치과재료학회지
2001
.06
SLA 처리 티타늄 표면에서의 유전자발현에 대한 상온대기압 플라즈마의 효과
서혜연
,
강민경
,
최유리
외 3명
대한치과재료학회지
2015
.03
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2015-510-001111720