In this paper, sliding wear tests of the 304 stainless steels were performed at room temperature varying sliding distance and applied load using a pin-on-disk wear tester. Worn surfaces and wear debris were analyzed using an XRD and observed by an SEM. Micro Vickers hardness was also measured as a function of depth from the worn surface to evaluate work hardening during the wear. Test results showed that the wear mode changed from mild wear to severe plasticity dominated wear (metallic particle oxidation, adhesive wear) as the sliding distance and the applied load increased. The change in the wear mechanism was associated with subsurface plastic deformation and work-hardening. Strain-induced martensitic transformation was observed on the sliding surface of the austenitic stainless steel. Relationship between the transformation and the work-hardening was explored and discussed.
목차
Abstract
1. 서론
2. 시험소재와 실험 방법
3. 결과 및 고찰
4. 결론
5. 참고문헌
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
이 논문과 함께 이용한 논문
물 윤활 환경에서 알루미나 세라믹의 마찰ㆍ마모 거동
구영필
,
김상준
,
김형자
외 2명
한국트라이볼로지학회 학술대회
2003
.06
자기입자와 전기화학 폴리싱을 통한 STS304의 국부적 표면분석
곽성웅
,
김욱수
,
이강현
외 1명
한국기계가공학회 춘추계학술대회 논문집
2020
.06
Improvement of Wear Behaviors of STS304 using Ultrasonic Surface Impact Treatment (USIT)
Li Liang
,
D. W. Lee
,
M. R. Kim
외 1명
한국정밀공학회 학술발표대회 논문집
2016
.10
최근 본 자료
댓글(0)
0