Mixtures type PCM, H₂O-NaOH that has relatively large capacity of the latent heat and long duration of phase change temperature was developed and experimentally analyzed for the low temperature storage of the food and medical products. The results could be summarized as follows;
1. Borax as nucleating agent and acrylic polymer as thickening agent were added to H₂O to prevent the supercooling and phase separation.
2. Phase change (solid?liquid) duration of H₂O added with NaOH was prolonged longer 50% than that of pure H₂O.
3. Phase change temperature of the latent heat material, H₂O-NaOH was 1.5∼2℃, the maximum latent heat was 279 kJ/kg at the NaOH addition of 1.3 wt. %.
4. The specific heat of H₂O-NaOH at the solid and liquid state was increased in proportion to the wt. % of NaOH, when NaOH of 1.15∼1.60 wt. % was added to H₂O, the specific heat of the solid state was increased from 3.19 kJ/kg to 5.84 kJ/kg and that of liquid state from 7.8 kJ/kg to 10.28 kJ/kg.
5. When NaOH of 1.15~1.60 wt.% was added to H₂O, the total heat storage capacity composed of sensible and latent heat was 313~331.3 kJ/kg and the maximum heat storage capacity was occurred at NaOH addition of 1.30 wt. %.
1. Borax as nucleating agent and acrylic polymer as thickening agent were added to H₂O to prevent the supercooling and phase separation.
2. Phase change (solid?liquid) duration of H₂O added with NaOH was prolonged longer 50% than that of pure H₂O.
3. Phase change temperature of the latent heat material, H₂O-NaOH was 1.5∼2℃, the maximum latent heat was 279 kJ/kg at the NaOH addition of 1.3 wt. %.
4. The specific heat of H₂O-NaOH at the solid and liquid state was increased in proportion to the wt. % of NaOH, when NaOH of 1.15∼1.60 wt. % was added to H₂O, the specific heat of the solid state was increased from 3.19 kJ/kg to 5.84 kJ/kg and that of liquid state from 7.8 kJ/kg to 10.28 kJ/kg.
5. When NaOH of 1.15~1.60 wt.% was added to H₂O, the total heat storage capacity composed of sensible and latent heat was 313~331.3 kJ/kg and the maximum heat storage capacity was occurred at NaOH addition of 1.30 wt. %.
목차
Abstract
기호설명
1. 서론
2. 재료 및 실험방법
3. 결과 및 고찰
4. 결론
참고문헌
참고문헌 (7)
참고문헌 신청
함께 읽어보면 좋을 논문
논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!
-
Development of Viscose Rayon Process (I. Dissolution of Cellulose in $CO_2$/NaOH System)
한국섬유공학회 학술발표논문집
1998 .01
-
Recycling Properties of NaOH Produced in $Ca(OH)_2-Na_2CO_3-NaOH$ System
한국자원리싸이클링학회 학술발표대회
2005 .01
-
NaOH 첨착활성탄의 H₂S 흡착능
대한환경공학회지
2000 .05
-
Electrochemical behaviour of Titanium in 1M NaOH solution
한국표면공학회 학술발표회 초록집
2004 .11
-
NaOH 화학적 활성화로 제조된 하이브리드 커패시터의 전기화학적 특성
화학공학
2013 .01
-
Polyaluminumchloride와 NaOH 첨가량에 따른 수산화알루미늄 합성에 관한 연구
화학공학
2010 .01
-
NaOH 처리 아마섬유의 구조 및 물리적 성질
한국섬유공학회지
1997 .01
-
NaOH 를 함침시킨 활성탄 흡착제의 H₂S 흡착 특성
대한환경공학회 학술발표논문집
1998 .12
-
Ethanol, NaOH, 온도 조합에 의한 활성탄의 경제적 재생기술 개발
대한환경공학회 학술발표논문집
1997 .12
-
개질 비대칭 폴리에테르이미드막을 통한 물-이소프로판올 혼합물의 투과증발 분리: 투과증발 특성에 미치는 표면층 개질에 사용된 NaOH 농도의 영향
공업화학
1999 .01
-
NaOH 처리농도에 따른 아마섬유의 결정구조 전이
한국섬유공학회 학술발표논문집
1997 .01
-
NaOH 첨가방법에 따른 알칼리 활성 슬래그 모르타르의 압축강도 및 유동 특성
한국콘크리트학회 학술대회 논문집
2012 .05
-
NaOH가 플라이애시 다량치환 경화 콘크리트의 강도회복에 미치는 영향
대한건축학회 학술발표대회 논문집
2020 .04
-
염색 전처리조의 NaOH 자동 농도 제어 시스템의 개발
한국염색가공학회지
2003 .08
-
NaOH가 고로슬래그 다량치환 경화 콘크리트의 강도회복에 미치는 영향
한국콘크리트학회 학술대회 논문집
2020 .06
-
Ethylene Glycol이 Poly(ethylene Terephthalate) 섬유의 알칼리 가수분해에 미치는 영향
한국섬유공학회지
1986 .01
-
Stress Relaxation of PET film in NaOH Solution
한국고분자학회 학술대회 연구논문 초록집
1986 .04
-
Study on the Stress Relaxation of PET Film in NaOH Solution
한국고분자학회 학술대회 연구논문 초록집
1986 .10
-
Ethanol, NaOH, 온도 조합에 의해 2차 재생된 활성탄의 물리 화학적 특성평가
대한환경공학회 학술발표논문집
1998 .12
이 논문의 저자 정보
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2009-563-018133096