- 대한용접·접합학회 International Journal of Korean Welding Society International Journal of Korean Welding Society Vol.2 No.2
- 발행연도
- 2002.12
- 수록면
- 14 - 18 (5page)
이용수
초록· 키워드
오류제보하기
Titanium and titanium alloy are excellent in corrosion resistance and specific intensity, and also in the biocompatibility. On the other hand, the brazing is bonding method of which productivity and reliability are high, when the complicated and precise structure of the thin plate is constructed. However, though conventional titanium-based brazing filler metal was excellent in bond strength and corrosion resistance, it was disadvantageous that metal structure and mechanical property of the base metal deteriorated, since the brazing temperature ( about IOOO°C ) is considerably high. Authors developed new brazing filler metal which added Zr to Ti-Cu (-Ni) alloy which can be brazed at 900°C or less about 15 years ago.
In this paper, the development of more low-melting-point brazing filler metal was tried by the addition of the fourth elements such as Ni, Co, Cr for the Ti-Zr-Cu alloy. As a method for finding the low-melting-point composition, eutectic composition exploration method was used in order to reduce the experiment point.
As the result, several kinds of new brazing filler metal such as 37.5Ti-37.5-Zr-25Cu alloy (melting point: 825°C) and 30Ti-43Zr-25Cu-2Cr alloy (melting point: 825°C) was developed. Then, the brazing joint showed the characteristics which were almost equal to the base metal from the result of obtaining metallic structure and strength of joint of brazing joint. However, the brazing filler metal composition of the melting point of 820°C or less could not be found. Consequentially, it was clarified that the brazing filler metal developed in this study could be practically sufficiently used from results such as metal structure of brazing joint and tensile test of the joint.
In this paper, the development of more low-melting-point brazing filler metal was tried by the addition of the fourth elements such as Ni, Co, Cr for the Ti-Zr-Cu alloy. As a method for finding the low-melting-point composition, eutectic composition exploration method was used in order to reduce the experiment point.
As the result, several kinds of new brazing filler metal such as 37.5Ti-37.5-Zr-25Cu alloy (melting point: 825°C) and 30Ti-43Zr-25Cu-2Cr alloy (melting point: 825°C) was developed. Then, the brazing joint showed the characteristics which were almost equal to the base metal from the result of obtaining metallic structure and strength of joint of brazing joint. However, the brazing filler metal composition of the melting point of 820°C or less could not be found. Consequentially, it was clarified that the brazing filler metal developed in this study could be practically sufficiently used from results such as metal structure of brazing joint and tensile test of the joint.
목차
Abstract
1.Introduction
2.Experimental mathod
3.Experimental results and discussion
4.Conclusion
References
참고문헌 (0)
참고문헌 신청함께 읽어보면 좋을 논문
논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!
-
BNi-2계 삽입금속에 의한 SUS304 스테인리스강 접합체의 강도와 조직에 미치는 브레이징 온도의 영향 : Ni기 삽입금속에 의한 브레이징 접합성의 기초적 검토(II)
한국재료학회지
2007 .01
-
Laser brazing molybdenum using two titanium base fillers
Advances in materials research : AMR
2012 .01
-
스테인리스강용 브레이징 합금과 브레이징 공정
대한용접·접합학회지
2012 .12
-
최신의 고능률 브레이징 기술개발 동향
대한용접·접합학회지
2016 .04
-
스테인리스강의 브레이징 특성
대한용접·접합학회지
2011 .12
-
D-Tube의 최적의 브레이징을 위한 평가
대한기계학회 춘추학술대회
2007 .10
-
Cu-8.6wt%Al 삽입금속을 사용한 페라이트계 스테인리스강의 아크 브레이징 접합부의 미세조직과 인장성질
대한용접·접합학회지
2011 .08
-
알미늄 저융점 브레이징을 위한 Al-Si-Cu계 filler metal 주조 조직에 미치는 첨가제의 영향
대한용접학회 특별강연 및 학술발표대회 개요집
2015 .05
-
Al-Si-Cu계 저융점 용가재를 사용한 열교환기용 알루미늄 브레이징에서 첨가제에 관한 연구
대한용접학회 특별강연 및 학술발표대회 개요집
2017 .11
-
대기 브레이징을 이용한 다이아몬드와 삽입금속의 접합특성과 그 응용
대한용접학회 특별강연 및 학술발표대회 개요집
2009 .04
-
진공브레이징에 의한 SUS304 스테인리스강과 BNi-2계 삽입금속의 접합특성 : Ni기 삽입금속에 의한 브레이징 접합성의 기초적 검토(I)
한국재료학회지
2007 .01
-
Active brazing of Al2O3 to copper using dual active Ag-Cu-Sn-Zr-Ti filler
대한용접학회 특별강연 및 학술발표대회 개요집
2019 .05
-
A357을 이용한 알루미늄 반응고 브레이징 접합 계면 특성
소성·가공
2012 .12
-
가스터빈용 초내열 합금의 고온 브레이징에 관한 연구
대한기계학회 춘추학술대회
2001 .08
-
Dissimilar laser brazing of sialon to WC-Co alloy using the Ag-Cu-Ti activated filler metal
대한용접학회 특별강연 및 학술발표대회 개요집
2012 .05
-
Ag계 Filler Metal을 사용한 YSZ와 STS430의 브레이징 접합시 Ti, Sn의 함량 변화가 접합강도에 미치는 영향
대한용접·접합학회지
2014 .02
-
진공 브레이징을 이용한 다이아몬드와 Ni계 페이스트의 계면 거동 연구
대한용접학회 특별강연 및 학술발표대회 개요집
2005 .06
-
Effects of Strain Rate and Temperature on Fracture Strength of Ceramic/Metal Joint Brazed with Ti-Ag-Cu Alloy
Journal of Mechanical Science and Technology
2002 .09
-
Wide gap brazing
대한용접학회 특별강연 및 학술발표대회 개요집
1992 .01
-
ZrO₂-Ti합금의 활성금속 브레이징
대한용접·접합학회지
2012 .06
이 논문의 저자 정보
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2009-581-014263080